Abstract The objective was to apply a simplex lattice design to determine the properties of polyvinyl alcohol-graft-lactic acid (PVA-g-LA) with different values for two independent variables: curing time (X1) and LA ratio (X2). Each independent variable was varied among three levels: –1, 0, and +1. Three coded levels were 120 min, 150 min, and 180 min for X1 and 2.5 g, 5 g, and 7.5 g for X2. Dependent variables of swelling behavior in various swelling media and thermal analysis parameters were monitored. The optimal formulation was selected based on the desirability value. The prediction was accurate, showing a low value of percent error. The morphology of the selected formulation with the highest desirability value showed a compact and dense film. Propranolol hydrochloride used as a model drug, was loaded into PVA-g-LA film. The propranolol hydrochloride content was 4.19 ± 1.05 mg/cm2. The cumulative release and permeation of drug were 61.94 ± 8.03% and 59.96 ± 6.61%, respectively. Thus, response surface methodology can be used as a tool to predict or optimize the process parameters for PVA-g-LA transdermal films in an accurate manner. PVA-g-LA could control the release and permeation of drug from the film layer.

Abstract The objectives of this study are to prepare a 5 wt% lidocaine/aspirin ionic liquid drug-loaded gelatin/polyvinyl alcohol composite film using a freeze-thaw procedure and to evaluate their physicochemical characteristics, in vitro drug release, and stability. Lidocaine/aspirin ionic liquid drugs can be prepared by an ion-pair reaction between the hydrochloride salts of lidocaine and the sodium salts of aspirin, which showed a significant change in their thermal properties when compared to those pure drugs. The results showed that a transdermal patch could feasibly be used in pharmaceutical transdermal patches with good physicochemical properties. A chemical interaction between the drug and polymer base was not found. Decomposition of the lidocaine/aspirin ionic liquid drug was found in the patch; however, the properties of the patch were not changed after drug loading. The patch controlled the drug release and showed good stability during the studied period of three months when kept at 4°C more than at ambient temperature and 45°C.